| Customization: | Available |
|---|---|
| CAS No.: | 24993-04-2 |
| Formula: | C18h37n3o5 |
|
Still deciding? Get samples of US$ 3300/Ton
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
PA6 E0760
| Product Description | Applications | ||||
| ·60%6 60% glass fiber reinforced PA6 | · Injection molding | ||||
| · Excellent heat stability | · Good mechanical properties balance | ||||
| Properties | Test Method | Test Condition | Unit | Typical Values | |
| Physical properties | |||||
| Specific Gravity | ISO 1183 | 23ºC | g/cm3 | 1.7 | |
| Ash | ISO 3451 | 800ºC,30min | % | 60 | |
| Mechanical properties | |||||
| Tensile Strength | ISO 527 | 50mm/min | MPa | 220 | |
| Elongation at Break | ISO 527 | 50mm/min | % | 1.5 | |
| Flexural Modulus | ISO 178 | 2mm/min | MPa | 20300 | |
| Charpy Notched Impact Strength | ISO 179-1eA | 23ºC | kJ/m2 | 15 | |
| Charpy Unotched Impact Strength | ISO 179-1eU | 23ºC | kJ/m2 | 75 | |
| Thermal properties | |||||
| Melting Point | DSC | - | C | 222 | |
| Other properties | |||||
| Flammability | TL1010 | - | mm/min | 15 | |
| Note: The data above is a typical value for reference, not a guaranteed value. The data will vary with tool design such as gate type, gate location, gate number, injection molding process, and part thickness. The data will vary with different colors as well. Prior to use the material, please consult with Topo New Material polymer. |
|||||
| Processing Conditions | Range | ||||
| Melt Temperature | 240-270ºC | ||||
| Mold Temperature | 50-80ºC | ||||
| Pre-Dry needed | 100ºC, 4-8h | ||||